5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

5290R 2W/mK Thermal Conductive Silicone Potting Compound 1:1 Mix Ratio

제품 상세정보:

원래 장소:	중국
브랜드 이름:	Huitian
인증:	ROHS REACH
모델 번호:	5290

상세 정보

원래 장소:

중국

브랜드 이름:

Huitian

인증:

ROHS REACH

모델 번호:

5290

색상 파트 A:

빨간색

색상 파트 B:

하얀색

점도 파트 A:

4,500 ~ 7,000 MPa · s

점착성 B 부분:

4,000 ~ 6,500 MPa · s

믹스 비율:

1 : 1

밀도 파트 A:

2.7 ~ 2.8 g/ml

밀도 부분 B:

2.7 ~ 2.8 g/ml

저장 수명:

6 개월

작업 온도:

-50-200 ℃

강조하다:

5290R thermal conductive potting compound , silicone potting compound 2W/mK , 1:1 mix ratio electronic potting

거래 정보

최소 주문 수량:

1000kg

가격:

협상 가능

포장 세부 사항:

20kg/set : A : 10kg/버킷, B : 10kg/버킷.

공급 능력:

100mt/month

제품 설명

5290R 2W High Thermal Conductive 1:1 Mix Red/White Silicone, UL94V-0, -50°C To 200°C

Ideal for electronics encapsulation, automotive module sealing, sensor potting & circuit board protection.

Product Overview

The 5290R(A9B9) is a high-performance, two-part addition-type potting silicone rubber designed for electronic and electrical applications. Combining exceptional thermal conductivity with excellent flow properties, this product offers both thermal management and mechanical protection. The red/white 1:1 mixing ratio ensures simple and consistent application.

Key Applications

Inverter Inductance: Provides thermal management and mechanical protection
Military Power Supplies: Ensures reliable performance in harsh environments
Communication Modules: Offers moisture-proof and shockproof protection
General Electronics: Suitable for transformers, capacitors, and PCBs

Product Features

High Thermal Conductivity

2 W/m*K thermal conductivity for efficient heat dissipation

Excellent Flow Properties

Viscosity range: 4,500-7,000 mPa*s (Part A), 4,000-6,500 mPa*s (Part B)

Dual Curing Mechanism

Cures at room temperature (≤6 hours) or accelerated with heat (≤30 minutes at 80°C)

Superior Insulation

Dielectric strength ≥13 KV/mm, volume resistivity ≥1.0×10^12 Ω*cm

Wide Temperature Range

Maintains elasticity from -50°C to 200°C

Safety Compliance

UL94V-0 flame retardant, RoHS compliant

Technical Specifications

Physical Properties Before Curing (25 ±2℃, 60%±5%RH)
Appearance (A)	-	Red flow
Appearance (B)	-	White flow
Viscosity (A)	mPa*s	4,500~7,000
Viscosity (B)	mPa*s	4,000~6,500
Density (A)	g/cm^3	2.7~2.8
Density (B)	g/cm^3	2.7~2.8
Curing Properties (A:B=1:1)
Operating Time	min	130±70
Curing Time (25℃)	h	≤6
Curing Time (80℃)	min	≤30
Physical Properties After Curing (A:B=1:1)
Hardness	Shore A	35~45
Dielectric Strength	KV/mm	≥13
Volume Resistivity	Ω*cm	≥1.0×10^12
Dielectric Constant (1.2MHz)	-	≥2.8
Thermal Conductivity	W/m*K	2±0.2

Application Instructions

Preparation

Stir Part A and Part B separately to ensure uniformity before mixing.

Mixing

Weigh components in 1:1 ratio and mix thoroughly for homogeneous consistency.

Defoaming

Natural Defoaming: Allow 20-30 minutes for air bubble release
Vacuum Defoaming: 5-10 minutes at -0.1 MPa vacuum

Potting

Apply to clean, dry surfaces while mixture maintains good flowability.

Curing

Room temperature or heat accelerated curing available. Higher temperatures reduce curing time.

Packaging & Storage

Packaging: 5290RA9 20kg/barrel, 5295RB9 20kg/barrel

Storage: 8-28°C in cool, dry location. 6 month shelf life when properly stored.

Safety Information

Store in sealed containers away from children. Avoid contact with N, P, S organic compounds and Sn, Pb, Hg, As ionic compounds which may inhibit curing. Consult MSDS for complete safety details.

Application example of 5290R Silicone Potting Compound

5290R Silicone Potting Compound packaging

Technical specifications of 5290R Silicone Potting Compound